HMLS 1100Dtex 2*3 3*3 Polyester cord Dipped Stiff Cord
High strength polyester dipped stiff cord has high strength, good adhesion, low shrinkage and high stability. Widely used in auto parts, timing belts, V-belts and other industrial products.
| Quantity: | |
|---|---|
-
kindom
| HMLS Polyester Dipped Stiff Cord | ||||||||||
| Test Item | Unit | 1000D/2*3 | 1500D/3*3 | 1000D/2*5 | 1000D/4*3 | 1000D/5*3 | 1000D/6*3 | 1000D/8*3 | 1000D/9*3 | 2000D/12*3 |
| Breaking Strength | N | ≥420 | ≥630 | ≥680 | ≥850 | ≥1020 | ≥1200 | ≥1680 | ≥1860 | ≥2400 |
| Elongation at Break | % | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 10±1.5 | 10±2.0 | 10±2.0 | 10±2.0 |
| Elongation at Setload | % | 3.1±0.5 | 2.0±0.5 | 2.2±0.5 | 2.4±0.6 | 2.0±0.6 | 2.2±0.6 | 2.4±0.6 | 2.3±0.6 | 2.0±0.6 |
| @200N | @200N | @200N | @300N | @300N | @400N | @500N | @500N | @500N | ||
| Weight per 100 m | g/100m | 73±3 | 110±4 | 121±4 | 145±5 | 185±6 | 217±7 | 287±10 | 327±15 | 436±15 |
| Cord Diameter | mm | 0.9±0.1 | 1.2±0.1 | 1.24±0.1 | 1.36±0.1 | 1.55±0.1 | 1.65±0.1 | 1.95±0.15 | 2.1±0.15 | 2.4±0.15 |
| Hot air Shrinkage 150℃ 3min 130g | % | ≤3 | ≤3 | ≤3 | ≤2.8 | ≤2.8 | ≤2.6 | ≤2.8 | ≤2.8 | ≤2.8 |
| T-Adhesion at150℃30min | N/cm | ≥240 | ≥260 | ≥280 | ≥300 | ≥320 | ≥350 | ≥400 | ≥420 | ≥480 |
| High Tenacity Polyester Dipped Stiff cord | |||||||||
| Test Item | 1000D/1*3 | 1000D/2*3 | 1000D/3*3 | 1000D/2*5 | 1000D/5*3 | 1000D/4*3 | 1000D/6*3 | 1000D/6*5 | |
| Breaking Strength | N | ≥210 | ≥440 | ≥650 | ≥720 | ≥1050 | ≥860 | ≥1250 | ≥2100 |
| Elongation at Break | % | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 10.0±2.0 |
| Elongation at Setload | % | 3.3±0.5 | 3.1±0.5 | 2.0±0.5 | 1.9±0.5 | 2.0±0.5 | 2.3±0.5 | 2.2±0.5 | 1.8±0.5 |
| @100N | @200N | @200N | @300N | @300N | @300N | @400N | @500N | ||
| Weight per 100 m | g/100m | 38±3 | 73±4 | 110±4 | 123±5 | 185±6 | 146±5 | 222±7 | 365±10 |
| Cord Diameter | mm | 0.68±0.1 | 0.95±0.1 | 1.15±0.1 | 1.25±0.1 | 1.5±0.1 | 1.65±0.1 | 1.95±0.15 | 2.1±0.15 |
| Hot air Shrinkage 150℃ 3min 130g | % | ≤3 | ≤3 | ≤3 | ≤2.8 | ≤2.8 | ≤2.6 | ≤2.8 | ≤2.8 |
| T-Adhesion at150℃30min | N/cm | ≥240 | ≥260 | ≥280 | ≥300 | ≥320 | ≥350 | ≥400 | ≥420 |
| HMLS Polyester Dipped Stiff Cord | ||||||||||
| Test Item | Unit | 1000D/2*3 | 1500D/3*3 | 1000D/2*5 | 1000D/4*3 | 1000D/5*3 | 1000D/6*3 | 1000D/8*3 | 1000D/9*3 | 2000D/12*3 |
| Breaking Strength | N | ≥420 | ≥630 | ≥680 | ≥850 | ≥1020 | ≥1200 | ≥1680 | ≥1860 | ≥2400 |
| Elongation at Break | % | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 10±1.5 | 10±2.0 | 10±2.0 | 10±2.0 |
| Elongation at Setload | % | 3.1±0.5 | 2.0±0.5 | 2.2±0.5 | 2.4±0.6 | 2.0±0.6 | 2.2±0.6 | 2.4±0.6 | 2.3±0.6 | 2.0±0.6 |
| @200N | @200N | @200N | @300N | @300N | @400N | @500N | @500N | @500N | ||
| Weight per 100 m | g/100m | 73±3 | 110±4 | 121±4 | 145±5 | 185±6 | 217±7 | 287±10 | 327±15 | 436±15 |
| Cord Diameter | mm | 0.9±0.1 | 1.2±0.1 | 1.24±0.1 | 1.36±0.1 | 1.55±0.1 | 1.65±0.1 | 1.95±0.15 | 2.1±0.15 | 2.4±0.15 |
| Hot air Shrinkage 150℃ 3min 130g | % | ≤3 | ≤3 | ≤3 | ≤2.8 | ≤2.8 | ≤2.6 | ≤2.8 | ≤2.8 | ≤2.8 |
| T-Adhesion at150℃30min | N/cm | ≥240 | ≥260 | ≥280 | ≥300 | ≥320 | ≥350 | ≥400 | ≥420 | ≥480 |
| High Tenacity Polyester Dipped Stiff cord | |||||||||
| Test Item | 1000D/1*3 | 1000D/2*3 | 1000D/3*3 | 1000D/2*5 | 1000D/5*3 | 1000D/4*3 | 1000D/6*3 | 1000D/6*5 | |
| Breaking Strength | N | ≥210 | ≥440 | ≥650 | ≥720 | ≥1050 | ≥860 | ≥1250 | ≥2100 |
| Elongation at Break | % | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 10.0±2.0 |
| Elongation at Setload | % | 3.3±0.5 | 3.1±0.5 | 2.0±0.5 | 1.9±0.5 | 2.0±0.5 | 2.3±0.5 | 2.2±0.5 | 1.8±0.5 |
| @100N | @200N | @200N | @300N | @300N | @300N | @400N | @500N | ||
| Weight per 100 m | g/100m | 38±3 | 73±4 | 110±4 | 123±5 | 185±6 | 146±5 | 222±7 | 365±10 |
| Cord Diameter | mm | 0.68±0.1 | 0.95±0.1 | 1.15±0.1 | 1.25±0.1 | 1.5±0.1 | 1.65±0.1 | 1.95±0.15 | 2.1±0.15 |
| Hot air Shrinkage 150℃ 3min 130g | % | ≤3 | ≤3 | ≤3 | ≤2.8 | ≤2.8 | ≤2.6 | ≤2.8 | ≤2.8 |
| T-Adhesion at150℃30min | N/cm | ≥240 | ≥260 | ≥280 | ≥300 | ≥320 | ≥350 | ≥400 | ≥420 |