Factory Wholesale High Tenacity Polyester Yarn
840DNylon yarn high tenacity dipped nylon yarn is in higher strength, good adhension, low shrinkage, high stability. Widely used in high-pressure rubber hose and others industrial products.
| Quantity: | |
|---|---|
-
kindom
| Dipped Nylon66 yarn | ||||||
| Test Item | Unit | 1260D/5*3 | 1260/3*3 | 1260D/7*3 | 1400D/9*3 | 3200D/1*3 |
| Breaking Strength | N | ≥1500 | ≥700 | ≥800 | ≥900 | ≥780 |
| Elongation at Break | % | 20±3.0 | 21±3.0 | 21±3.0 | 22±3.0 | ≤5.0 |
| Elongation at | % | 5.5±1.0 | 5.5±1.0 | 5.5±1.0 | 5.5±1.0 | |
| Weight per 100 m | g/100m | 233 | 138 | 293 | 436 | 66±4.0 |
| Cord Diameter | mm | 1.65±0.03 | 1.15±0.05 | 2.10±0.05 | 2.50±0.05 | 1.15±0.05 |
| Hot air Shrinkage 150℃ 3min | % | ≤5.0 | ≤5.0 | ≤5.0 | ≤5.0 | ≤5.0 |
| T-Adhesion at150℃30min | N/cm | ≥160 | ≥180 | ≥180 | ≥180 | ≥180 |
| Dipped Nylon66 yarn | ||||||
| Test Item | Unit | 1260D/5*3 | 1260/3*3 | 1260D/7*3 | 1400D/9*3 | 3200D/1*3 |
| Breaking Strength | N | ≥1500 | ≥700 | ≥800 | ≥900 | ≥780 |
| Elongation at Break | % | 20±3.0 | 21±3.0 | 21±3.0 | 22±3.0 | ≤5.0 |
| Elongation at | % | 5.5±1.0 | 5.5±1.0 | 5.5±1.0 | 5.5±1.0 | |
| Weight per 100 m | g/100m | 233 | 138 | 293 | 436 | 66±4.0 |
| Cord Diameter | mm | 1.65±0.03 | 1.15±0.05 | 2.10±0.05 | 2.50±0.05 | 1.15±0.05 |
| Hot air Shrinkage 150℃ 3min | % | ≤5.0 | ≤5.0 | ≤5.0 | ≤5.0 | ≤5.0 |
| T-Adhesion at150℃30min | N/cm | ≥160 | ≥180 | ≥180 | ≥180 | ≥180 |