2000D/2High Module Low Shrinkage 100% Polyester Tire Cord Fabric
Tire cord fabric is very low weft density of the fabric,look like curtain,the warp bears load ,weft hold the warp. Normally it can be used in tire cord,air spring, rubber products,helping with the great shock load and strong vibration.420D Tire cord is the star product in our company,which is frequently used in the whole industry.
| Color: | |
|---|---|
| Quantity: | |
-
kingdom
| Dipped polyester tyre cord fabric | |||||
| Item | Unit | 1000D/2 (1100dtex/2) | 1300D/2 (1440dtex/2) | 1500D/2 (1670dtex/2) | 2000D/2 (2200dtex/2) |
| Breaking strength (min) | N/end | 140 | 180 | 205 | 270 |
| Elongation at 44.1N | % | 4.5± 1.0 | |||
| Elongation at 58.0N | % | 4.5±1.0 | |||
| Elongation at 66.6N | % | 4.5±1.0 | |||
| Elongation at 88.2N | % | 4.5±1.0 | |||
| Elongation at 100N | % | ||||
| Adhesion(H-test)(min) | N/cm | 125 | 135 | 140 | 170 |
| Breaking strength difference(max) | % | 4 | 4 | 4 | 4 |
| Breaking elongation difference(max) | % | 5 | 5 | 5 | 5 |
| Dip pick up | % | 3.5±1 | 3.5±1 | 3.5±1 | 3.5±1 |
| Breaking elongation(min) | % | 14 | |||
| Diameter | mm | 0.56±0.03 | 0.61±0.03 | 0.66±0.03 | 0.75±0.03 |
| Pingle twist(Z) | T/10cm | 45±1.5 | 40±1.5 | 37±1.5 | 33±1.5 |
| Ply twist (S) | T/10cm | 45±1.5 | 40±1.5 | 37±1.5 | 33±1.5 |
| Hot air shrinkage 177℃*2min*0.05CN/dtex(min) | % | 2 | 2 | 2 | 2 |
| Elongation @Breaking of weft yarn(min) | % | 120 | 120 | 120 | 120 |
| Dipped polyester tyre cord fabric | |||||
| Item | Unit | 1000D/2 (1100dtex/2) | 1300D/2 (1440dtex/2) | 1500D/2 (1670dtex/2) | 2000D/2 (2200dtex/2) |
| Breaking strength (min) | N/end | 140 | 180 | 205 | 270 |
| Elongation at 44.1N | % | 4.5± 1.0 | |||
| Elongation at 58.0N | % | 4.5±1.0 | |||
| Elongation at 66.6N | % | 4.5±1.0 | |||
| Elongation at 88.2N | % | 4.5±1.0 | |||
| Elongation at 100N | % | ||||
| Adhesion(H-test)(min) | N/cm | 125 | 135 | 140 | 170 |
| Breaking strength difference(max) | % | 4 | 4 | 4 | 4 |
| Breaking elongation difference(max) | % | 5 | 5 | 5 | 5 |
| Dip pick up | % | 3.5±1 | 3.5±1 | 3.5±1 | 3.5±1 |
| Breaking elongation(min) | % | 14 | |||
| Diameter | mm | 0.56±0.03 | 0.61±0.03 | 0.66±0.03 | 0.75±0.03 |
| Pingle twist(Z) | T/10cm | 45±1.5 | 40±1.5 | 37±1.5 | 33±1.5 |
| Ply twist (S) | T/10cm | 45±1.5 | 40±1.5 | 37±1.5 | 33±1.5 |
| Hot air shrinkage 177℃*2min*0.05CN/dtex(min) | % | 2 | 2 | 2 | 2 |
| Elongation @Breaking of weft yarn(min) | % | 120 | 120 | 120 | 120 |