1890D Factory Directly Wholesale Twisted Nylon Spandex Yarn
High strength polyester dipped stiff cord has high strength, good adhesion, low shrinkage and high stability. Widely used in auto parts, timing belts, V-belts and other industrial products.
| Quantity: | |
|---|---|
-
kindom
| HMLS Polyester Dipped Stiff Cord | ||||||||||
| Test Item | Unit | 1000D/2*3 | 1500D/3*3 | 1000D/2*5 | 1000D/4*3 | 1000D/5*3 | 1000D/6*3 | 1000D/8*3 | 1000D/9*3 | 2000D/12*3 |
| Breaking Strength | N | ≥420 | ≥630 | ≥680 | ≥850 | ≥1020 | ≥1200 | ≥1680 | ≥1860 | ≥2400 |
| Elongation at Break | % | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 10±1.5 | 10±2.0 | 10±2.0 | 10±2.0 |
| Elongation at Setload | % | 3.1±0.5 | 2.0±0.5 | 2.2±0.5 | 2.4±0.6 | 2.0±0.6 | 2.2±0.6 | 2.4±0.6 | 2.3±0.6 | 2.0±0.6 |
| @200N | @200N | @200N | @300N | @300N | @400N | @500N | @500N | @500N | ||
| Weight per 100 m | g/100m | 73±3 | 110±4 | 121±4 | 145±5 | 185±6 | 217±7 | 287±10 | 327±15 | 436±15 |
| Cord Diameter | mm | 0.9±0.1 | 1.2±0.1 | 1.24±0.1 | 1.36±0.1 | 1.55±0.1 | 1.65±0.1 | 1.95±0.15 | 2.1±0.15 | 2.4±0.15 |
| Hot air Shrinkage 150℃ 3min 130g | % | ≤3 | ≤3 | ≤3 | ≤2.8 | ≤2.8 | ≤2.6 | ≤2.8 | ≤2.8 | ≤2.8 |
| T-Adhesion at150℃30min | N/cm | ≥240 | ≥260 | ≥280 | ≥300 | ≥320 | ≥350 | ≥400 | ≥420 | ≥480 |
| HMLS Polyester Dipped Stiff Cord | ||||||||||
| Test Item | Unit | 1000D/2*3 | 1500D/3*3 | 1000D/2*5 | 1000D/4*3 | 1000D/5*3 | 1000D/6*3 | 1000D/8*3 | 1000D/9*3 | 2000D/12*3 |
| Breaking Strength | N | ≥420 | ≥630 | ≥680 | ≥850 | ≥1020 | ≥1200 | ≥1680 | ≥1860 | ≥2400 |
| Elongation at Break | % | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 9.5±1.5 | 10±1.5 | 10±2.0 | 10±2.0 | 10±2.0 |
| Elongation at Setload | % | 3.1±0.5 | 2.0±0.5 | 2.2±0.5 | 2.4±0.6 | 2.0±0.6 | 2.2±0.6 | 2.4±0.6 | 2.3±0.6 | 2.0±0.6 |
| @200N | @200N | @200N | @300N | @300N | @400N | @500N | @500N | @500N | ||
| Weight per 100 m | g/100m | 73±3 | 110±4 | 121±4 | 145±5 | 185±6 | 217±7 | 287±10 | 327±15 | 436±15 |
| Cord Diameter | mm | 0.9±0.1 | 1.2±0.1 | 1.24±0.1 | 1.36±0.1 | 1.55±0.1 | 1.65±0.1 | 1.95±0.15 | 2.1±0.15 | 2.4±0.15 |
| Hot air Shrinkage 150℃ 3min 130g | % | ≤3 | ≤3 | ≤3 | ≤2.8 | ≤2.8 | ≤2.6 | ≤2.8 | ≤2.8 | ≤2.8 |
| T-Adhesion at150℃30min | N/cm | ≥240 | ≥260 | ≥280 | ≥300 | ≥320 | ≥350 | ≥400 | ≥420 | ≥480 |